Title: Development of corrosion layer of steel bar in concrete and its mechanical and electrochemical effects

Authors: Yingshu Yuan, Yongsheng Ji

Addresses: School of Civil Engineering, China University of Mining and Technology, Xuzhou, Jiangsu, 221008, P.R. China. ' School of Civil Engineering, China University of Mining and Technology, Xuzhou, Jiangsu, 221008, P.R. China

Abstract: Steel bar in concrete can be corroded under environment of chloride attack. The rust which has a characteristic of expansion and the porosity of the steel-concrete interface offer a space for diffusing of the expansive rust. The diffusion of the rust transforms the porous steel-concrete interface into the dense mixed layer composed of concrete and rust, the layer is called corrosion layer in this paper. The development of the corrosion layer leads to mechanical effect on corrosion cracking and electrochemical effect on retardation of oxygen and water transportation. The dense corrosion layer resists rust diffusion and produces an expansive force which finally forms corrosion cracking. The dense corrosion layer retards transporting oxygen and water to the surface of the steel bar and then the corrosion rate slows down. This paper describes the composition and distribution of the corrosion layer along the bar surface, presents the distribution model of expansive force and reveals time depended process of the variation of corrosion rate of the steel bar in concrete and discusses the mechanism of mechanical and electrochemical effects.

Keywords: chloride attack; steel-concrete interface; corrosion cracking; corrosion rate; time-depended process; concrete; steel bars; structural engineering; rust; porosity; mechanical effects; electrochemical effects.

DOI: 10.1504/IJSTRUCTE.2010.031486

International Journal of Structural Engineering, 2010 Vol.1 No.2, pp.199 - 206

Published online: 05 Feb 2010 *

Full-text access for editors Full-text access for subscribers Purchase this article Comment on this article