Microstructure and total oxidising capacity for m-xylene of La1-xCaxCoO3 nanoparticles synthesised by combustion method Online publication date: Tue, 30-Jan-2018
by Nguyen Xuan Dung; Phan Thi Minh Huyen; Luu Tien Hung; Steffen Schulze; Michael Hietschold
International Journal of Nanotechnology (IJNT), Vol. 15, No. 1/2/3, 2018
Abstract: Nanoparticles of La1-xCaxCoO3 (x = 0, 0.1, 0.3 and 0.5) perovskites were synthesised by the combustion method using glycine agent and corresponding metal nitrates. The perovskites were characterised by thermogravimetric and differential thermal analysis (TG-DTA) and Brunauer-Emmett-Teller (BET) adsorption isotherms. The microstructure of samples was characterised by X-ray diffraction (XRD) combined with transmission electron microscopy (TEM), selected area electron diffraction (SAED) and energy dispersive X-ray (EDX). The grain size ranges from 20 nm to 30 nm. A high surface area from 15 m2/g to 21 m2/g was achieved for samples annealed at relatively low temperature (600°C). The perovskites exhibit a good catalytic activity in total oxidation of m-xylene at low reaction temperature.
Online publication date: Tue, 30-Jan-2018
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Nanotechnology (IJNT):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email firstname.lastname@example.org