Investigation on slurry erosion of Al2O3 incorporated glass/epoxy composites Online publication date: Wed, 06-Jan-2021
by Ajith G. Joshi; M. Prasanna Kumar; S. Basavarajappa
International Journal of Surface Science and Engineering (IJSURFSE), Vol. 14, No. 4, 2020
Abstract: The jet erosion of fibre reinforced plastics (FRPs) has been reported in many literatures available, but very few have reported on their slurry erosion behaviour of FRPs. Furthermore, limited studies have paid attention on slurry erosion characterisation of filler incorporated FRPs. Hence, present study was focused on slurry erosion behaviour of alumina fillers incorporated glass/epoxy composites. The parameters considered were slurry concentration, contact angle and impact velocity. The experimental results reveal that increase in filler percentage increased the erosion resistance of glass/epoxy composites. The increase in slurry concentration and impact velocity has resulted in higher amount of erosion of studied composites. The material loss due to erosion increased with increase of impact angle till 45°, whereas further increase in impact angle caused reduction in wear. Erosion mechanisms were studied through SEM image of eroded samples. Worn surface analysis revealed that plastic deformation, matrix debonding with microcutting, microploughing, and pulverisation were dominant erosion mechanisms at 45° to 60° impact angle.
Online publication date: Wed, 06-Jan-2021
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Surface Science and Engineering (IJSURFSE):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email firstname.lastname@example.org