Corrosion in viewpoint of metal microstructure for grey and ductile cast iron in HCl solutions and presence of thiourea
by Sayed S. Abd El Rehim, Sayed H. El-Nekhaly, Ahmed El Essawy Abdou
International Journal of Microstructure and Materials Properties (IJMMP), Vol. 2, No. 3/4, 2007

Abstract: Two types of cast iron were employed in this work. Grey cast iron was the first type, and ductile was the second one. Two specimens of the grey cast iron sample were used; one was kept without heat treatment, and the second was completely heat-treated by ferritisation regime. The two specimens of ductile cast iron were used similarly; one was kept without heat treatment grey and the second was ferritised by heat treatment. Potentiodynamic technique was applied for collecting corrosion data of the above four metal specimens in HCl solutions in the absence and presence of thiourea as an inhibitor. The measurements were performed in different concentrations of HCl (0.05, 0.2, 0.5, and 1 M) at 20ºC and in the absence of an inhibitor, on the other hand, corrosion parameters were collected in 0.2 M HCl at different temperature levels (20ºC, 30ºC, 40ºC, and 50ºC). Thiourea was added in different concentrations to 0.2 M HCl at 25ºC, then corrosion data was deduced. An optical microscope was used to investigate the microstructure of grey and ductile cast iron before and after heat treatment. Corrosion resistance and corrosion rates were collected directly from potentiostat, where Tafel lines were applied to the software. The above raw data was used to deduce activation thermodynamic parameters (Ea*, ΔHº, and ΔSº) of dissolution processes in the absence of thiourea by applying Arhenius equation. Adsorption parameters, in the presence of thiourea, were deduced using the kinetic model and the Flory-Huggins isotherms were used as inhibition mechanisms for the investigation before and after treatment.

Online publication date: Sun, 07-Oct-2007

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Microstructure and Materials Properties (IJMMP):
Login with your Inderscience username and password:

    Username:        Password:         

Forgotten your password?


Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com