High temperature corrosion behaviour of HVOF sprayed WC-CrC-Ni coatings Online publication date: Tue, 05-Jul-2016
by B. Somasundaram; Ravikiran Kadoli; M.R. Ramesh; C.S. Ramesh
International Journal of Surface Science and Engineering (IJSURFSE), Vol. 10, No. 4, 2016
Abstract: The present work aims to study the hot corrosion resistance of high velocity oxy-fuel (HVOF) sprayed WC-CrC-Ni coating developed on three types of boiler tube materials such as SA213-T22, MDN-310 and Superfer 800 H steels. Hot corrosion studies were conducted in a molten salt environment of Na2SO4-60%V2O2 at 700°C and thermogravimetric analysis was used to establish kinetics of corrosion. Corrosion kinetics of coated steels followed nearly parabolic behaviour and showed a lower corrosion rate in comparison to uncoated alloys. It is concluded that corrosion is restricted to the external surface of the coating and the formation of thick scale composed of oxides of Cr, Ni and their spinel oxides, acts as a diffusion barrier to the transportation of corrosive species into the coating. The carbides of tungsten and chromium uphold the strength of the coating.
Online publication date: Tue, 05-Jul-2016
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Surface Science and Engineering (IJSURFSE):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email firstname.lastname@example.org