Effect of austempering temperature on microstructure and properties of austempered ductile iron Online publication date: Fri, 04-Jan-2019
by C.F. Han; W.Q. Zhou; Y.F. Sun; J.T. Ma
International Journal of Microstructure and Materials Properties (IJMMP), Vol. 13, No. 5, 2018
Abstract: The influence of austempering temperature on microstructure and properties of Austempered Ductile Iron were studied in this paper. The purpose was to improve comprehensive performance of Austempered Ductile Iron for adapting to slurry pump transflux parts. The nodularisation grade of graphite was 2-3 magnitude and the size of graphite was 6-7 magnitude. After austempered at different temperatures for 120 min, the microstructure mainly consisted of acicular ferrite, retained austenite and spheroidal graphite. With increasing austempering temperature, tensile strength improved firstly and then decreased, impact toughness increased, the wear resistance became worse, and the corrosion resistance increased. When the heat treatment process was 900°C × 90 min + 250°C × 120 min, the comprehensive performance was better (tensile strength: 1710 MPa, elongation: 2%, impact toughness: 40 J/cm2, Brinell hardness: 467 HBW, wear weightlessness rate: 0.17 mg/m) than the requirements in ASTM A897-06.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Microstructure and Materials Properties (IJMMP):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com
Our Blog 
Follow us on Twitter 
Visit us on Facebook