Experimental investigation of damage and fracture in glassy materials at the nanometre scale Online publication date: Tue, 04-Apr-2006
by D. Bonamy, S. Prades, L. Ponson, D. Dalmas, C.L. Rountree, E. Bouchaud, C. Guillot
International Journal of Materials and Product Technology (IJMPT), Vol. 26, No. 3/4, 2006
Abstract: Slow crack advance is observed in real time via an Atomic Force Microscope in a minimal glass, amorphous Silica, under stress corrosion. Fracture proceeds through the nucleation, growth and coalescence of damage cavities, as recently reported in an aluminosilicate glass. The crack growth velocity as observed at the continuum scale is shown to be dominated by accelerating phases corresponding to the cavity coalescence with the main crack front. The process zone at the crack tip is then determined, and shown to increase with time when both the average crack growth velocity and the mechanical stress are kept constant. Transport of water molecules within the process zone is conjectured to be the dominant mechanism responsible for this time evolution. Migration of alkali Na ions in more complex Silicate glass is finally evidenced at the sub-mocrometric scale by observing through AFM the crack propagation in binary Na2O/SiO2 glasses.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Materials and Product Technology (IJMPT):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com
Our Blog 
Follow us on Twitter 
Visit us on Facebook