Desilication of fly ash and development of lightweight construction blocks from alkaline activated desilicated fly ash Online publication date: Fri, 06-Oct-2017
by Thabo Falayi; Felix Ndubisi Okonta; Freeman Ntuli
International Journal of Environment and Waste Management (IJEWM), Vol. 20, No. 3, 2017
Abstract: Massive reserves of power plant fly ash dumps in South Africa have necessitated the development of different processes for effective remediation to achieve zero waste generation by secondary processes. Silica was leached from fly ash (FA) at the optimum conditions of a leaching time of 6 h, 3 M KOH, 500 rpm agitation speed, 25 liquid to solid ratio and a leaching temperature of 100°C. A lightweight construction block (LWCB) was developed from desilicated fly ash (DFA) and KOH. It was found that the optimum synthesis conditions were 10 M KOH, +0.075-0.300 mm DFA and a curing temperature of 40°C for 12 h, 80°C for 12 h and 100°C for 24 h. The development of strength was through the formation of Kalsilite. The LWCB met the minimum requirements for ASTM C34-13, C129-14a and South African standard (SANS227: 2007).
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Environment and Waste Management (IJEWM):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com