Investigation of electrical transport properties in heterojunctions comprised of silicon substrate and nanocrystalline iron disilicide films
by Nathaporn Promros; Phongsaphak Sittimart; Weerasaruth Kaenrai
International Journal of Nanotechnology (IJNT), Vol. 13, No. 10/11/12, 2016

Abstract: In this study, n-type nanocrystalline FeSi₂/p-type Si heterojunctions were fabricated using facing-target direct-current sputtering (FTDCS). The possible transportation mechanisms of carriers were investigated by analysing the dark J-V characteristics at temperatures ranging between 60 and 300 K. The ideality factor (n) was estimated from the slope of the linear region for the forward lnJ-V characteristics. The value of n was 1.87 at 300 K and nearly constant at temperatures ranging from 140 to 300 K, suggesting that a recombination process at the junction interface was dominant in the transportation mechanism of carriers. At temperatures below 140 K, the value of n increased by more than two and the value of A was virtually constant. Owing to the consistency of A, combined with the temperature dependent value of n, the implication is that a trap-assisted multi-step tunnelling mechanism governed the carrier transport. From the analysis of J-V characteristics, the value of barrier height was 0.58 eV at 300 K and decreased to 0.19 eV at 60 K.

Online publication date: Wed, 16-Nov-2016

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Nanotechnology (IJNT):
Login with your Inderscience username and password:

Username:        Password:          Forgotten your password?

Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com