Hydrothermal rutile to anatase reverse phase transformation
by C. McNicoll; T. Kemmitt; V. Golovko
International Journal of Nanotechnology (IJNT), Vol. 11, No. 5/6/7/8, 2014

Abstract: TiO₂ sols peptised with oxalic acid were synthesised with oxalic acid ratios from 0.25 to 1.0 oxalic acid per titanium. The resulting transparent colloidal sols of TiO₂ contained a mixture of phases and sizes of TiO₂ particles depending on the oxalic acid content. The sols were hydrothermally treated at different temperatures ranging from 85°C to 275°C. Treatment below 100°C produced mostly anatase, while the decomposition of the oxalic acid between 120°C and 170°C allowed a phase change to rutile, with a rapid crystallite size increase from around 10 nm to 40 nm. AT-FTIR confirmed the complete decomposition of organic acids within the sols treated at 220°C. Very limited rutile crystallite growth was observed above this temperature. However, sols produced with the lower oxalic acid content remained as rutile while those produced using higher initial oxalic: Ti ratios (0.5 and 1.0 M equivalents) induced a reverse phase transformation back to anatase phase TiO₂. High resolution SEM showed that the anatase phase TiO₂ crystallites grew to around 30 nm at the highest temperature used (275°C) having indistinct morphology, while the rutile phase TiO₂ were elongated rods growing up to 100 nm.

Online publication date: Mon, 15-Dec-2014

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Nanotechnology (IJNT):
Login with your Inderscience username and password:

Username:        Password:          Forgotten your password?

Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com