Influences of deposition power of GZO thin films on the properties of the heterojunction diode based on a NiO/GZO bi-layer structure
by Chia-Cheng Huang; Fang-Hsing Wang; Cheng-Fu Yang; Hong-Hsin Huang
International Journal of Nanotechnology (IJNT), Vol. 11, No. 1/2/3/4, 2014

Abstract: A compound of ZnO with 3 wt% Ga₂O₃ (ZnO : Ga₂O₃ = 97 : 3 in wt%, GZO) was sintered at 1400°C as a GZO target. Radio frequency magnetron sputtering was used to deposit nickel oxide thin films (NiO, deposition power of 100 W) and GZO thin films (deposited at 300°C by changing the deposition power from 50 W to 150 W) on glass substrates to form p(NiO)-n(GZO) heterojunction diodes with high transmittance. The structural, optical, and resistivity properties of the GZO and NiO thin films and NiO/GZO heterojunction devices were investigated with scanning electron microscopy (SEM), X-ray diffraction (XRD) patterns, UV-visible spectroscopy, Hall-effect analysis, and current-voltage (I-V) analysis. XRD analysis showed that only the (111) diffraction peak of NiO and the (002) and (004) diffraction peaks of ZnO (GZO) were observable in the NiO/GZO heterojunction devices, and the GZO thin films showed a good c-axis orientation perpendicular to the glass substrates. The variations in the optical band gap (E_g value) of the GZO thin films were evaluated from the plots of (αhv) = c(hv - E_g)^1/2, revealing that the measured E_g value decreased with increasing deposition power. For the deposited GZO thin films, both the carrier concentration and mobility linearly decreased and the resistivity increased approximately with increasing deposition power. When the sputtering deposition power for the GZO thin films was deposited at different power, the I-V characteristics confirmed that a p-n junction characteristic was successfully formed in the NiO/GZO heterojunction devices.

Online publication date: Sat, 15-Nov-2014

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Nanotechnology (IJNT):
Login with your Inderscience username and password:

Username:        Password:          Forgotten your password?

Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com