Microwave-assisted synthesis of highly active nanosized ceria-zirconia solid solutions for CO oxidation
by D. Das, G. Thrimurthulu, K. Lakshmi, B.M. Reddy
International Journal of Nanotechnology (IJNT), Vol. 7, No. 9/10/11/12, 2010

Abstract: Superior ceria-zirconia (Ce_xZr_1−xO₂; 1 : 1 mole ratio) solid solution was synthesised by employing a poly-block copolymer surfactant combined with microwave treatment. For comparison purpose an identical composition ceria-zirconia solid solution was also prepared by a conventional coprecipitation method. The structural and textural characteristics of the synthesised samples were investigated using X-ray diffraction (XRD), Raman spectroscopy (RS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), BET surface area, and BJH pore size distribution (PSD) methods. The catalytic activity was evaluated for CO oxidation at normal atmospheric pressure. The XRD measurements revealed the presence of cubic Ce_0.75Zr_0.25O₂ and Ce_0.6Zr_0.4O₂ phases in the conventional coprecipitation and surfactant-controlled microwave treated samples, respectively. The Ce_xZr_1−xO₂ solid solution prepared by surfactant-controlled microwave-assisted method exhibited a high specific surface area and mesoporosity. The SEM images suggested that all samples consist of typical spherical agglomerates with almost uniform size within the nanometer range. The TEM measurements revealed that the nanosized crystallites are in the narrow range between 4 nm and 8 nm and densely packed. Raman measurements revealed existence of more oxygen vacancies in the surfactant-controlled microwave treated sample. Interestingly, the Ce_xZr_1−xO₂ solid solution obtained by surfactant-controlled microwave treatment exhibited better CO oxidation activity than the conventional coprecipitated sample. Enhanced activity of the surfactant-controlled microwave treated sample is correlated with smaller crystallite size, mesoporosity, and more number of defects.

Online publication date: Tue, 17-Aug-2010

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Nanotechnology (IJNT):
Login with your Inderscience username and password:

Username:        Password:          Forgotten your password?

Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com