Alumina-YAG composites: preparation, experimental characterisation and numerical modelling
by V. Cannillo, P. Palmero, T. Manfredini, L. Montanaro
International Journal of Materials and Product Technology (IJMPT), Vol. 35, No. 3/4, 2009

Abstract: Al₂O₃/YAG composite powders have been synthesised by reverse strike precipitation. The powders were characterised by DTA/TG simultaneous analysis; the phase evolution was studied by XRD analysis, while the crystallite formation and growth were followed by TEM observations. A fully dense, homogenous material was obtained by sintering 900°C pre-treated powders at 1600°C for 3 h. For limiting grain growth, both a doping with 500 ppm MgO followed by a free sintering and a fast sintering procedure involving a high heating rate (50°C/min) were performed. The sintered bodies were then characterised by SEM observation and Vickers indentation. Moreover, a numerical model was employed in order to estimate the mechanical properties of the composite materials starting from their microstructural features and from the single constituent phase properties.

Online publication date: Sat, 23-May-2009

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Materials and Product Technology (IJMPT):
Login with your Inderscience username and password:

Username:        Password:          Forgotten your password?

Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com