Fatigue strength of hard-chromium-plated handlebars Online publication date: Thu, 20-Nov-2008
by Alessandro Guglielmotti, Carmine Lucignano, Fabrizio Quadrini, Erica Anna Squeo, Federica Trovalusci
International Journal of Surface Science and Engineering (IJSURFSE), Vol. 2, No. 5, 2008
Abstract: Prototypes of handlebars for motorcycles were fabricated by rotary bending and hard-chromium electrodeposition. Fatigue tests were carried out on rough handlebars and hard-chromium plated handlebars; the former resisted over 200.000 cycles, the latter failed at about 50.000 cycles. Scanning Electron Microscopy (SEM) allowed one to observe the presence of sub-surface cracks, which probably originated during the tube bending. Moreover numerical simulation permitted one to identify the occurrence of buckling during the bending process. The combination of buckling, cracks and residual stresses from the chromium electrodeposition results in a very poor behaviour of the handlebar under fatigue test.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Surface Science and Engineering (IJSURFSE):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com