Thermomigration in lead-free solder joints
by Mohd F. Abdulhamid, Shidong Li, Cemal Basaran
International Journal of Materials and Structural Integrity (IJMSI), Vol. 2, No. 1/2, 2008

Abstract: In the next generation nanoelectronics and SiC based electronic packaging, current density and temperature gradient will be larger in orders of magnitude. Electromigration and thermomigration are considered to be major road blocks leading to realisation of nanoelectronics and SiC based high temperature power electronics. In this paper, damage mechanics of 95.5Sn4Ag0.5Cu (SAC405) lead-free solder joints under high temperature gradients have been studied. This paper presents observations on samples which were subjected to 1000°C/cm thermal gradient for two hours, 286 hours, 712 hours and 1156 hours. It was observed that samples subjected to thermal gradient did not develop a Cu3Sn intermetallic compound (IMC) layer at the hot side due to Cu migration to the cold side thus causing insufficient Cu mass concentration to form Cu3Sn. On the other hand, in samples subjected to isothermal annealing exhibited IMC growth. In samples subjected to thermomigration, near the cold side the Cu concentration is significantly higher, compared to hot side. Extensive surface hardness testing showed increase in hardness from the hot to cold sides, which indicates vacancy migration and Sn grain coarsening are in the opposing direction.

Online publication date: Sat, 21-Jun-2008

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Materials and Structural Integrity (IJMSI):
Login with your Inderscience username and password:

    Username:        Password:         

Forgotten your password?


Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com