Influence of aging on microstructure and toughness of die-casting die steels Online publication date: Mon, 16-Jun-2008
by G. Cornacchia, M. Gelfi, M. Faccoli, R. Roberti
International Journal of Microstructure and Materials Properties (IJMMP), Vol. 3, No. 2/3, 2008
Abstract: This study investigates the modification of the carbide type, size, shape and the associated changes in the toughness properties after prolonged aging at temperatures close to that of maximum hardening during tempering treatment. The aging effects on the microstructure of both steels still consist of a tempered martensite matrix, with an increased amount of precipitates and more marked prior austenitic grain boundaries. For H13 steel, the aging effects on fracture toughness show an appreciable increase in up to 50 h treatment; raising the aging time to 250 h causes considerable embrittlement. For H11 steel, however, the fracture toughness decreases early, from the first stages of aging; this behaviour has been associated with an increase in the carbide size. At increasing aging time, also for H11 steel, the embrittlement of prior austenite grain boundaries prevails in controlling fracture initiation and in decreasing fracture toughness.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Microstructure and Materials Properties (IJMMP):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com
Our Blog 
Follow us on Twitter 
Visit us on Facebook