Femtosecond laser-triggered electrical discharges at nanoprobe tips for nanoprocessing Online publication date: Fri, 25-Apr-2008
by J. Chen, D.F. Farson, S.I. Rokhlin
International Journal of Nanomanufacturing (IJNM), Vol. 1, No. 6, 2007
Abstract: Electrical discharges were stimulated by femtosecond laser pulses in nanoscale gaps between sharpened metal tips and gold film. Laser pulses with intensity 5.6 × 1011 W/cm² reliably triggered discharges in sub-micron and microscale gaps. For gaps shorter than a threshold value, the discharge stimulation probability was near unity, over a range of applied potentials. At a lower laser intensity of 3.5 × 1011 W/cm² the discharge stimulation probability characteristics were similar to those at higher intensity, but only for the higher applied potentials (60–80V) used. At lower applied potential, the discharge probability was also lower and depended on potential. With current limiting diode, the discharge current reached a peak value in about 2ns, and extinguished after an additional 2–3ns. Scanning Electron Microscopy studies show that micron-sized gold surface region were melted and re-solidified by the electrical discharge.
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Nanomanufacturing (IJNM):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email subs@inderscience.com