Effect of low-temperature isothermal holding on microstructure and mechanical properties of hot rolled high carbon Nb microalloyed steel plate
by Indrajit Dey; Rajib Saha; Swarup Kumar Ghosh
International Journal of Materials and Product Technology (IJMPT), Vol. 62, No. 1/2/3, 2021

Abstract: Two high carbon steels, one plain carbon (HC0) and the other, Nb microalloyed (HC1) are selected in the present research. Both experimental steels were initially hot rolled after complete homogenisation and then air cooled to room temperature. These hot rolled plates were then subjected to low temperature isothermal holding followed by air-cooling to room temperature. Isothermal holding above the martensite start temperature (Ms) results in the formation of bainite with some amount of high carbon martensite whereas, isothermal holding below Ms leads to the formation of predominantly martensite. The increase in isothermal holding temperature from 200°C to 300°C results in lowering the hardness, estimated yield strength and ultimate tensile strength values marginally for HC0 whereas, it decreases the hardness, estimated yield strength and ultimate tensile strength values significantly for HC1 steel which may be attributed to the expected formation of some amount of coarse niobium carbide (NbC).

Online publication date: Mon, 24-May-2021

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Materials and Product Technology (IJMPT):
Login with your Inderscience username and password:

Username:        Password:          Forgotten your password?

Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com