Electromagnetic wave absorbing characteristics of C/Co-Mn and C/Co-Zn doped barium hexaferrite sandwiched nanocomposites
by Rodziah Nazlan; Ismayadi Ismail; Idza Riati Ibrahim; Fadzidah Mohd Idris; Mohamad Ashry Jusoh; Khamirul Amin Matori
International Journal of Nanotechnology (IJNT), Vol. 17, No. 11/12, 2020

Abstract: The development of high reflection loss and broad frequency bandwidth for microwave absorbing materials (MAMs) has been intensified in recent years. Carbon nanocomposites have stimulated attention as the EM-wave absorbing materials due to their high conductivity with high dissipating capability of electrostatic charges and EM-wave radiation shielding. In this study, we report on the analysis of microwave absorption through absorption spectrum of carbon/barium hexaferrite nanocomposites with Co-Mn and Co-Zn as dopants. The nanoparticles of Co-Mn-doped and Co-Zn-doped barium hexaferrites were synthesised using the mechanical alloying technique. The resultant particles were then mixed thoroughly with epoxy resin with ratio of 8:92 wt.% prior to sandwich with carbon black layer at different thicknesses of 1, 2 and 3 mm to form nanocomposites. The samples were characterised on their morphological, magnetic and microwave properties using field emission scanning electron microscope (FESEM), vibrating sample magnetometer (VSM) and vector network analyser (VNA) respectively; there follow rational discussions on the effect of dopant substitutions and microstructure on the absorption/reflection loss and bandwidth broadening of MAM. The results show that the saturation magnetisation of BaCoZnFe₁₆O₂₇ is higher as compared to that of BaCoMnFe₁₆O₂₇ and pure BaFe₁₂O₁₉ in which Zn behaves as an ion modifier that compensates the magnetic moment in hexaferrite sublattices, thus translated into an increase of net magnetic moment per unit volume of the sample. By using carbon black as a matching layer and BaCoMnFe₁₆O₂₇ as an absorbing layer with total sandwich thickness of 2 mm, the highest reflection loss of 39.83 dB was obtained. The capability to tune the absorption and bandwidth of all the samples at various frequencies indicates that these materials would be a superior MAM. Through scrutinisation of relationship between absorption/reflection loss with different dopants and thickness variation, further discussion on mechanism of adsorption/reflection characteristics for research optimisation would be provided.

Online publication date: Wed, 13-Jan-2021

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Nanotechnology (IJNT):
Login with your Inderscience username and password:

Username:        Password:          Forgotten your password?

Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com