Evaluation of mechanical performance of friction welded AISI304L grade stainless steel joints Online publication date: Sun, 16-Sep-2018
by K. Umanath; K. Palanikumar
International Journal of Heavy Vehicle Systems (IJHVS), Vol. 25, No. 3/4, 2018
Abstract: Austenitic stainless steel (ASS) rods of AISI304L Grade when welded have the significant issue of hot breaking and loss of erosion resistance. To reduce these problems the solid state friction welding is the best way to weld the AISI304L alloy and required testing is needed for the further process. In this research work, friction welded AISI304L rods of 10 mm diameter have been used for conducting the experimental testing of tensile strength (TS), fatigue strength (FS), hardness strength and temperature transformation during the friction welding. The results obtained show that the maximum tensile strength of the friction welded joint is 532 MPa, which is equivalent to 94.16% of the base metals tensile strength. The fatigue strength of the notched specimens is lower than un-notched specimens due to the high crack propagation in notched specimens.
Online publication date: Sun, 16-Sep-2018
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Heavy Vehicle Systems (IJHVS):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email firstname.lastname@example.org