Some studies on three-body abrasive wear behaviour of hardfaced steel alloy for agricultural plough tool application
by A.R. Annappa; S. Basavarajappa
International Journal of Abrasive Technology (IJAT), Vol. 7, No. 3, 2016

Abstract: The influences of hardfacing deposit and deep cryogenic treatment on three-body abrasive wear behaviour of AISI 1013 steel were studied. The three-body abrasive wear tests were carried out using the dry sand/rubber wheel test rig as per ASTM G65 standard. Hardfacing was done by manual arc welding using ZEDALLOY VB hardfacing electrode. The deep cryogenic treatment was carried by using liquid nitrogen temperature at −196°C. The applied load, sliding velocity and sliding distance were considered as process parameters. Experimental results reveal that the hardfacing deposit showed the highest abrasive wear resistance as compared to deep cryotreated material. Worn-out surface observation by SEM witnessed same behaviour. The nature of material removal was microploughing or microcutting depending on the attack angle, due to cracks formed on the surface of material.

Online publication date: Fri, 29-Jul-2016

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Abrasive Technology (IJAT):
Login with your Inderscience username and password:

    Username:        Password:         

Forgotten your password?


Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com