The study on kinetics of metadynamic recrystallisation of a Nb-V microalloyed non-quenched and tempered steel Online publication date: Fri, 22-May-2020
by Liwen Zhang; Wenfei Shen; Chi Zhang; Yingnan Xia; Xinhua Shi; Fei Xia
International Journal of Computational Materials Science and Surface Engineering (IJCMSSE), Vol. 9, No. 1, 2020
Abstract: The metadynamic recrystallisation (MDRX) behaviour of a Nb-V microalloyed non-quenched and tempered steel was investigated by isothermal hot compression tests on Gleeble-1500 thermal-mechanical simulator. Compression tests were performed using double hit schedules at temperatures of 1,273-1,423 K, strain rates of 0.01-5 s−1, initial grain sizes of 92-149 μm and inter-pass time of 0.5-10 s. The effects of deformation parameters, including deformation temperature, strain rate, initial grain size and inter-pass time, on MDRX softening fraction were analysed. The experimental results show that MDRX softening fraction increases with the increase of deformation temperature, strain rate and inter-pass time, while it decreases with the increase of initial grain size. Based on the experimental results, the kinetic model of MDRX for the tested steel was established. A good agreement between the experimental and predicted MDRX softening fraction indicates that the established kinetic model can precisely predict the MDRX softening fraction for the tested steel.
Online publication date: Fri, 22-May-2020
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Computational Materials Science and Surface Engineering (IJCMSSE):
Login with your Inderscience username and password:
Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.
If you still need assistance, please email email@example.com