The luminescent properties of GdAlO3:Tb3+ phosphors based on molten salts addition
by Jinkai Li; Wenzhi Wang; Zongming Liu
International Journal of Nanomanufacturing (IJNM), Vol. 15, No. 1/2, 2019

Abstract: The (Gd1−xTbx)AlO3 (x = 0-0.12) were obtained through ammonium bicarbonate co-precipitation technology. The pure-phase (Gd1−xTbx)AlO3 with good dispersion could be obtained at relatively lower temperature of 1,000°C. Under optimum UV excitation into 275 nm, the photoluminescence (PL) spectra display a series of 5D4−7FJ transitions of Tb3+ in (Gd1−xTbx)AlO3 system with the strongest green emission at ~546 nm. The overlapping between 8S7/2−6IJ intra f-f transition of Gd3+ and 4f8-4f75d1 transition of Tb3+ at 275 nm suggesting the Gd3+ → Tb3+ energy transfer, and the quenching contents of Tb3+ was found to be ~10 at%. The luminescent property of GdAlO3:Tb3+ phosphor could be further improved with molten salt incorporation. The optimal composition of molten salts was determined to be the mixture of NaCl/Na2SO4 (5 wt% NaCl), and the mass ratio of mixture molten salts to precursor was 2:1. The relationship between the luminescent property and molten salts composition were studied in detail.

Online publication date: Mon, 07-Jan-2019

The full text of this article is only available to individual subscribers or to users at subscribing institutions.

 
Existing subscribers:
Go to Inderscience Online Journals to access the Full Text of this article.

Pay per view:
If you are not a subscriber and you just want to read the full contents of this article, buy online access here.

Complimentary Subscribers, Editors or Members of the Editorial Board of the International Journal of Nanomanufacturing (IJNM):
Login with your Inderscience username and password:

    Username:        Password:         

Forgotten your password?


Want to subscribe?
A subscription gives you complete access to all articles in the current issue, as well as to all articles in the previous three years (where applicable). See our Orders page to subscribe.

If you still need assistance, please email subs@inderscience.com